1. Raztopina za kaljenje vzmeti
The strain spring tempering solution refers to applying a tensile stress equivalent to 20 percent to 40 percent of the tensile strength at both ends of the tempered steel wire. The steel wire causes a small amount of strain under the tension effect, and the dislocation line moves. At this time, the interstitial solute atoms ( C and N atoms) diffuse to the vicinity of the dislocation line by means of temperature, "pinning" the moving dislocation. The carbides dispersed and precipitated during the whole tempering process showed a large number of pinning points, which made the dislocation "pinning" more thorough and sufficient, improved the plastic deformation resistance of the steel wire, and improved the elastic reduction characteristics of the steel wire.
2. Rešitev za ogrevanje indukcijske vzmeti
Indukcijska vzmet ima hitro segrevanje, površina jeklene žice je rahlo oksidirana, ni lahko povzročiti razogljičenja, zrna pa so tudi rafinirana. Trdnost in žilavost ter lastnosti elastičnosti so zelo dobre, teža pa se lahko zmanjša za 10 do 20 odstotkov pod pogojem, da se različni indikatorji vzmeti ohranijo na prvotni ravni. Za vzmetna jekla, ki vsebujejo vanadij in niobij, je mogoče uporabiti le višjo temperaturo avstenitizacije za popolno raztapljanje vanadija in niobija, pri čemer je mogoče doseči dejanski učinek kaljenja sekundarnega utrjevanja. Pri običajnem standardu ogrevanja je temperatura avstenitizacije previsoka, zrna jeklene žice so hrapava, močno pa se povečata tudi površinska oksidacija in razogljičenje, kar resno vpliva na življenjsko dobo. Pri indukcijskem segrevanju na 800 1000 stopinj jeklena žica ni nagnjena k razogljičenju, hudi oksidaciji in hrapanju zrn. Zato lahko indukcijsko ogrevanje v celoti izkoristi prednosti vzmetnega jekla, ki vsebuje vanadij in niobij.